Description
Description
This resin is synthesized through reactions of phenyl, methylchlorosilane, and special silane monomers.The various temperature resistant coatings formulated with this series of resins can be self dried at room temperature or baked for 1 hour at 120C ± 5 ° C. Energy saving, especially suitable for painting large equipment and workpieces that cannot be baked. The paint film is full, glossy, and has high hardness. Good heat resistance, light color, fast drying, and beneficial for assembly line production. 8801A resin can be formulated into a heat-resistant coating with a heat resistance of 500-600 ℃.
|
Code |
Appearance |
Visocsity25℃ (coat 4 cup)S |
Sold content% |
Dry time |
Heat Resistance |
Features & Appication |
|
8801A |
Slightly yellow to yellow transparent liquid |
30~60 |
50±2 |
Dry surface for 2h
Actual Dry 24h |
8801A (500 ℃± 5 ° C) 4h No foaming No cracking, Not falling off Slightly discolored
|
The various temperature resistant coatings formulated with this series of resins can be self dried at room temperature or baked for 1 hour at 120C ± 5 ° C. Energy saving, especially suitable for painting large equipment and workpieces that cannot be baked. The paint film is full, glossy, and has high hardness. Good heat resistance, light color, fast drying, and beneficial for assembly line production. 8801A resin can be formulated into a heat-resistant coating with a heat resistance of 500-600 ℃. |
|
8801A-1 |
8801A-1 has better temperature resistance than 8801A, can withstand light colored paint at 500-600 ℃, and has higher self drying hardness. Among other similar products in China, it has higher self drying hardness and better yellowing. |
|||||
|
8801-400 |
8801-400 This resin can be formulated into a heat-resistant coating with a heat resistance of around 400 ℃. The surface dries quickly, the paint film is full, and the gloss is good. |
|||||
|
8801C |
8801C resin can be formulated into a heat-resistant coating with a heat resistance of around 300 ℃. The paint film dries quickly and has good gloss. Among them, 8801C-3 has a higher cost performance ratio. |
|||||
|
8801B-1 |
The heat-resistant coating that can be formulated with 8801B-1 resin belongs to the fast drying type, which has faster drying properties than any other type. The surface drying time is only about five minutes, which is particularly suitable for primer and topcoat that require quick drying. It can be formulated into a quick drying and hot coating at 300-400 ℃. |
1. This resin series is soluble in organic solvents such as toluene, xylene, lipids, ketones, etc.
2. When using this resin, avoid mixing substances such as acid, alkali, salt, etc., otherwise it will affect the product performance.